● Chemical composition:

C: ≤ 0.15

Silicon Si: ≤ 1.00

Manganese Mn: ≤ 1.00

Sulfur s: ≤ 0.030

Phosphorus P: ≤ 0.040

Chromium Cr: 11.50 ~ 13.50

Nickel Ni: (≤ 0.60)

● Use:

Frozen Container Frame and exterior materials, automobile exhaust pipe (below 800℃), heat-resistant equipment parts.

Low ●SUS410 stainless iron problem:

SUS410 is nickel-free stainless steel, 1Cr13 is stainless iron, and it needs annealing before processing standard parts.

SUS410 is a Japanese brand; 1Cr13 is the corresponding China brand; X10Cr13 is the corresponding German brand; 410 is the corresponding American brand.

410 is only a member of the stainless steel family. As far as 410 is concerned, it can be divided into 0Cr13 and 1Cr13, depending on the use, which material is used.

410S is a kind of steel which improves the corrosion resistance and formability of 410 steel.

410F2 is a lead free-cutting steel that does not reduce the corrosion resistance of 410 steel.

410J1 is a high-strength steel that further improves the corrosion resistance of 410 steel, and is used for turbine blades and high-temperature components.

Characteristics of AISI410 stainless steel：

It is magnetic under both annealing and hardening conditions.

When heated in different ways, it will produce a wide range of properties.

Good corrosion resistance to acids: xiao acid, sulfuric acid, etc.